Styron EMERGE? 4702-15 Polycarbonate

Polymer,Thermoplastic,Polycarbonate (PC)

Styron

 PDF物性文檔下載

產(chǎn)品說明:

EMERGEa?￠ PC 4702-15 advanced resin is formulated with 20% glass fiber and a proprietary flame retardant package. It provides good ignition resistance, rigidity, dimension stability and heat resistance. 

Applications:

• Information Technology Equipment

• Power Tools

• Electrical Appliances and Parts

Information provided by Dow

This product line was spun off from Dow Chemical to Styron in 2010.

Styron EMERGE? 4702-15 Polycarbonate 物性表

物理性能	額定值 (公制)	額定值 (英制)	測試方法
比重	1.37 g/cc	1.37 g/cc	ASTM D792
填料含量	20 %	20 %	Glass; ASTM 5630B
線性成型收縮率	0.0020 - 0.0040 cm/cm	0.0020 - 0.0040 in/in	ASTM D955
熔體流動速率	15 g/10 min @Load 1.20 kg, Temperature 300 °C	15 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238

機械性能	額定值 (公制)	額定值 (英制)	測試方法
極限抗拉強度	79.3 MPa	11500 psi	0.125 in, injection molded, unannealed; ASTM D638
伸長率 (斷裂)	4.0 %	4.0 %	0.125 in, injection molded, unannealed; ASTM D638
拉伸模量	5.86 GPa	850 ksi	0.125 in, injection molded, unannealed; ASTM D638
懸壁梁缺口沖擊強度	0.721 J/cm	1.35 ft-lb/in	ASTM D256
懸壁梁無缺口沖擊強度	3.68 J/cm	6.90 ft-lb/in	ASTM D256

電氣性能	額定值 (公制)	額定值 (英制)	測試方法
相比耐漏電起痕指數(shù)(CTI)	175 V @Thickness 2.00 mm	175 V @Thickness 0.0787 in	IEC 60112

熱性能	額定值 (公制)	額定值 (英制)	測試方法
Hot Ball Pressure Test	>= 125 °C	>= 257 °F	IEC 60335-1
載荷下熱變形溫度(1.8 MPa)	135 °C	275 °F	unannealed; ASTM D648
	146 °C	295 °F	annealed; ASTM D648
維卡軟化溫度	146 °C	295 °F	50°C/hr, 50N; ASTM D1525
UL RTI	120 °C	248 °F	UL 746
UL RTI，機械沖擊	105 °C	221 °F	UL 746
UL RTI，機械無沖擊	120 °C	248 °F	UL 746
可燃性(UL94)	V-0	V-0	0.0625 in
	V-0	V-0	0.125 in
灼熱絲試驗	960 °C @Thickness 2.00 mm	1760 °F @Thickness 0.0787 in	IEC 60695-2-10

加工性能	額定值 (公制)	額定值 (英制)	測試方法
加工（熔體）溫度	288 - 316 °C	550 - 601 °F
模具溫度	82.0 - 116 °C	180 - 241 °F
干燥溫度	121 °C	250 °F
干燥時間	3 - 4 hour	3 - 4 hour