LLDPE 中石化廣州 DNDA-7144瓶蓋 涂覆  

 

陶氏線性低密度聚乙烯 DNDA-7144 NT 7

Linear Low Density Polyethylene Resin

The Dow Chemical Company

產(chǎn)品說(shuō)明：

• Injection molding

• Large industrial containers and trash cans

• Excellent low temperature impact strength, rigidity, stress crack resistance and processability

• Very narrow molecular weight distribution

• Complies with

• U.S. FDA 21 CFR 177.1520 (c)3.1a

• CANDIAN HPFB NO OBJECTION ( WITH LIMITATIONS)

• EU, No 10/2011

• U.S. FDA -DMF

• Consult the regulations for complete details.

DOW DNDA-7144 NT 7 Linear Low Density Polyethylene (LLDPE) Resin is produced using UNIPOL? PE Process Technology and is intended for use in injection molding applications such as large industrial containers and trash cans. This resin has been designed to have excellent impact strength, rigidity, environmental stress crack resistance and processability.

附加功能

 

陶氏線性低密度聚乙烯 DNDA-7144 NT 7 物性表

基本信息
機(jī)構(gòu)評(píng)級(jí)	DMF 未評(píng)級(jí) FDA 21 CFR 177.1520(c) 3.1a HPFB (加拿大) No Objection 2 歐洲 No 10/2011
形式	粒子
加工方法	注射成型

物理性能	額定值	單位制	測(cè)試方法
比重	0.924	g/cm3	ASTM D792
熔流率（熔體流動(dòng)速率） (190°C/2.16 kg)	20	g/10 min	ASTM D1238
抗環(huán)境應(yīng)力開裂 (50°C, 100% Igepal, F50)	20.0	hr	ASTM D1693

硬度	額定值	單位制	測(cè)試方法
肖氏硬度 (邵氏 D)	50		ASTM D2240

機(jī)械性能	額定值	單位制	測(cè)試方法
抗張強(qiáng)度			ASTM D638
屈服	11.7	MPa	ASTM D638
斷裂	7.58	MPa	ASTM D638
伸長(zhǎng)率			ASTM D638
屈服	3.0	%	ASTM D638
斷裂	60	%	ASTM D638
彎曲模量 - 2% 正割	386	MPa	ASTM D790B

沖擊性能	額定值	單位制	測(cè)試方法
拉伸沖擊強(qiáng)度 1	168	kJ/m2	ASTM D1822

熱性能	額定值	單位制	測(cè)試方法
載荷下熱變形溫度 (0.45 MPa, 未退火)	42.8	°C	ASTM D648
脆化溫度	< -76.1	°C	ASTM D746
維卡軟化溫度	93.9	°C	ASTM D1525
溶融溫度（DSC）	123	°C	內(nèi)部方法
結(jié)晶峰溫度 (DSC)	108	°C	內(nèi)部方法

補(bǔ)充信息
根據(jù) ASTM D 4976 進(jìn)行基板模制和測(cè)試。

備注
1 .	類型 S